SDC Handmade Blades

You can just ask the owner of this one to have a go.

- Kumamoto Hinoki / TC160 / Balsa / TC160 / Kumamoto Hinoki
- 73g
- 8.3mm
- 1940Hz
- Balance: 1.5cm (Very Low)

Originally Posted by Haraold

does this blade hve a lot of Flex?
awesome work as always!

No, this one is stiff as a brick!

Sent from my MAR-LX1A using Tapatalk

Originally Posted by hipnotic

You can just ask the owner of this one to have a go.- Kumamoto Hinoki / TC160 / Balsa / TC160 / Kumamoto Hinoki- 73g- 8.3mm- 1940Hz- Balance: 1.5cm (Very Low)

Originally Posted by Haraold

does this blade hve a lot of Flex?awesome work as always!

Originally Posted by hipnotic

No, this one is stiff as a brick!Sent from my MAR-LX1A using Tapatalk

This one definitely looks like it would scare opponents out of their shoes.

How fast is it?

Originally Posted by Haraold

yeah thought so,so almost no flex at all?

Very little bending if that's what you mean, but there is some out-of-plane deformation due to the thin textreme-carbon. That gives some sense of softness, which compensates for the high stiffness to some degree.

Originally Posted by UpSideDownCarl

This one definitely looks like it would scare opponents out of their shoes.

How fast is it?

Not having tried it myself I can't pinpoint exactly, but I've seen it look down on a Primorac Carbon.

This is not a blade for spin. It's relatively stiff, but quite slow on the Willow side, which will produce low arc disruptive shots by using LP's. The Spruce side, supported by a hard Rosewood layer, will help finishing the point using fast and direct shots.

Available FS.

- Spruce / Rosewood / Balsa / Ayous / Willow
- 69.6g
- 6.5mm
- 157x150mm
- STSQ (27.5x22.5x100mm)
- 1335Hz
- 2.1cm (Very Low)

Custom order, based on a Nittaku Goriki but with a standard head size.

- Walnut / Walnut / Walnut / Walnut / Walnut
- 101.2g
- 5.1mm
- 990Hz
- Balance: 3.0cm (Med)

Originally Posted by hipnotic

Custom order, based on a Nittaku Goriki but with a standard head size.

- Walnut / Walnut / Walnut / Walnut / Walnut
- 101.2g
- 5.1mm
- 990Hz
- Balance: 3.0cm (Med)

Too heavy and too slow, but extremely handsome...

Cheers
L-zr

Originally Posted by Lazer

Too heavy and too slow, but extremely handsome...

Cheers
L-zr

Well, it is a defensive blade...

Sent from my MAR-LX1A using Tapatalk

Originally Posted by hipnotic

Well, it is a defensive blade...

Sent from my MAR-LX1A using Tapatalk

Yes unfortunately, but still very handsome...

Wow that's a big S! 😁 The blade is based on a Ovtcharov ALC, inner fiber with a bigger head size and a thicker core. However, this is a very light specimen, which will of course compromise power, but at the same time makes it very nimble for close to the table play.

- Limba / Ayous / ALC / Ayous / ALC / Ayous / Limba
- 80.4g
- 6.2mm
- 158x152mm
- ST (98x24x28mm)
- 1356Hz
- Balance: 3.0cm (Med)

Custom order

- Poplar / Ayous / I-C / Ayous / I-C / Ayous / Poplar
- 88g
- 5.8mm
- 1230Hz
- Balance: 2.2cm (Low/Very Low)

Custom order asymmetric blade.

- Smoked Eucalyptus / Ayous / TC90 / Ayous / Ayous / SZLC / limba
- 86.2g
- 5.75mm
- 1442Hz
- Balance: 2.4cm (Low)

Fast, low throw, compact feeling and head size.

Available FS.

- Limba / A-C / Limba / WRC / Limba / A-C / Limba
- 86.8g
- 5.9mm
- 155x150mm
- ST (102x28.5x23mm)
- 1464Hz
- Balance: 3.9cm (High)

Originally Posted by backspacer

How long does it take you to make a blade, from planning to getting the materials and assembling it

Trade secret 😉

Originally Posted by Haraold

saw your instagramm Post,you already postet the fastest blade you ever built?

Kind of... It's similar to one that I've already posted, but this one was faster.

Sent from my MAR-LX1A using Tapatalk