Thanks for the clarification. I'm sure you mean the materials you use. So if I don't need a synthetic material primarily for speed, but just for stiffness, where speed gain is more undesirable, would you recommend the Spectra material?

And where would you please rank Aramid without carbon and Spectra? In terms of stiffness and speed.

Hello, I would like to discuss one more thing. Which of the following synthetic materials in a five-layer construction will create the greatest stiffness? Glass-fiber, Diolen-fiber, Diolen-carbon, Aramid-fiber, Spectra, Innegra-carbon Which of these materials also results in the lowest...

In the article you used these two contradictory statements in one paragraph. Vibration is essentially a rapid bending in both directions. Therefore, the blade cannot be flexible and have low vibrations at the same time. It can either be not very flexible and have low vibrations, or vice versa...

I am looking for a blade in this specification. Can you advise me?

I am looking for more detailed specifications of the STIGA Azalea Offensive blade. I am mainly interested in the overall thickness of the blade, the composition of the individual layers of the blade, and also the feel. Does the blade behave more flexily when using the ball, or does it have a...

Don't really understand your blade labeling. Specifically JOOLA Tezzo Paladin. For this blade you have described flex 8. This means the highest value of all the blades you sell. However, this blade has internal carbon and in addition the total thickness as you state is 6.8 mm. In contrast, the...

I also couldn't find anything about a blade that has hinoki layers and a koto center. Can you send me a link to this blade? Can you also list the thickness of this blade? Thank you.

Stiff, so that it doesn't have elasticity, but at the same time soft to the touch of the ball. Yes, something like Nobilis, but I would need a much slower one. Can you send me a link where there is more information about your IAC?

Hi, can you recommend a blade from your company that is stiff but slow. Preferably with a soft feel. I wouldn't want a blade with a synthetic insert.

Hi, can you recommend a blade from your company that is stiff but slow. Preferably with a soft feel. I wouldn't want a blade with a synthetic insert.

Does anyone know what type of artificial insert is used in this blade?

This blade is not made in the ST grip.

I also looked at the blade, somewhere they say that the artificial fiber is carbon, somewhere else they say that it is Black Cloth. Neottec does not define the type of artificial insert.

I thought that the seven-layer construction has a larger proportion of glue, which theoretically could add rigidity to the entire assembly even with a lower thickness. But I haven't verified this.

Defensive blades have a problem that they usually have a larger head and are thinner overall. So they are usually very flexible. But if you know of any such blades that are stiff and slow please post them.

Or I thought how to slow down while keeping the blade stiff is to choose a seven-ply wood with a smaller thickness. What do you think? I have a Fextra 7 blade, but at 6.25 mm thick it is still fast for my game.

Are you speaking from personal experience or general knowledge? I prefer slower. For example, I read about Neotec woodoo classic that it is very flexible.

All the blades you mentioned are seven-ply. Do you know of any blades with similar properties that are five-ply?

My problem with Chinese blades is that they are mostly made in FL grip. I need ST grip. Does anyone know if the Sanwei Fextra 5 is stiff or flex? I have the Fextra 7, it is stiff, but fast and a bit hard for me.