I changed mine now for the fourth time and had several splinters on the sponge. Without sealant it happened with the first change already. Not deep, so i could still use it but visible.

I guess you can go for the Yinhe. Otherwise there are several componies who went the path of the structure of a viscaria/tb or w/e alc. Just browse for it and you can find anything for any budget like 729 blue, dhs tg 506x... For now im sticking with yinhe but i dont really like how the...

Well i guess you cant go much lower with your budget as smth like you already use. Maybe with xiom on your backhand instead of andro. Xiom Vega Pro was my choice for example. And as long as you dont play the national Version on your fh you should be fine here too. Maybe you could go with smth...

I guess Stiga Mantra, Tibhar MX-P, Andro Rasanter R 47 and there might be a decent alternative from Xiom... This board does have Xiom expert. Lets just wait until he arrives, he will know better than in do in at least this case^^

I guess it depends more on how often you gonna reglue or maybe even boost your rubbers if any sealent is needed (besided of the kind of blade you are using - some you really have to seal it). In my experience with several blade - if you glue often and boost, you have to seal that blade...

Just to make it clear before anyone misunderstands this. "Blue is for smash" - These rubbers are damn tacky, and therefore not recommended for smashing at all. If you want to hit with this rubber loop or perform a topsping. Never smash. If you want to smash a really high ball, go and "twiddle"...

They are nearly the same rubber. At least in terms of what you arw asking. The blue one though is way more unforgiving. Hard to predict for the opponent, which is good. But if you play without a developed close to perfect fh technique, the rubber alone will show you that. I wouldnt recommend...

That is pretty much the full magic here you are describing. In comparison to China, Germany for example does nearly nothing for this sport. We have cities who deny the usage of our sport halls in the vacation. On top of that, the amount of money to maintain them is disgustingly low. Scouting...

Big thanks for that insight. There was a lot of interesting information.

I like to disagree here quite hard actually. Nearly every player who plays against FZD frequently is avoiding his fh. If you watch the first games he played in the last 2 tournaments at least, you can see why. They all try to play fh ralleys against him. His backhand though is quite deadly but...

It depends... First of all there is noch good receipt to boost out there, which involves complete undoming. So every boosted rubber has to be domed by the time the tutorial tells you to glue the boosted rubber. Normally you wait for around 1-2 days after your last layer of booster before you...

Has anyone played with the new DHS TG-506X? And could give a quick review/compare it with other blades? https://a.aliexpress.com/_B0djGB https://www.prott.vip/Product-Details.aspx?productcode=TG506X Thank you!

Falco TLB Seamoon doesnt last that long. But everything depends in that department. How often did you already boost that rubber, how often did you play with it, how many layers did you put on. How did you boost the rubber... What im trying to say is that you shouldnt consider what others are...

Never had that problem. But my rubber never survived more than 2 boosting processes. Maybe you will get there eventually. Because after every process i had to cut more from the rubber to make it fit to the blade. But at the beginning you wont get there. At least if you stick to one way of boosting

I guess depending on how hard you gonna go with you change, the only thing you will notice is that you need to change your technique and maybe hit harder. I mean that change is no big deal and not expensive to experience. Just buy smth like big dipper or a training rubber from 729 and see if...

Sponge is way to orange to yellowish for a tenergy or dignics. Same actually for wang chuqin as i just saw. Justinfoomh is at least right according his backhand rubber.

https://dhs-729.eu/de/belaege/43-492-belag-dhs-neo-hurricane-3.html#/26-farbe-schwarz/28-dicke-215_mm/34-harte_des_schwammes-38_40_mittel_hart This one would have been the neo commercial version. Yeah you can get at least similar results. Like i said in another post, the neo Version is just...

FZD, Wang Chuqin, Lin Gaoyuan, Xu Xin, Cheng Meng and probably some more are still using tenergy or dignics

Ok that is new to me. Whats is the experience with dhs if it "goes bad"? Does the glue not work anymore or what. Im asking because i have mine for over a year now (the big bottle) and it is still doing its job. At least i think it is lol Although im wondering - maybe that is the reason why...

You can read about this in the interview with DHS: https://ooakforum.com/viewtopic.php?t=35876 In summary this means that the commercial version has probably less to zero quality control, so the sheets you get can differ quite much in terms of hardness and therefore feel. In case i chose to...