The harder you chose your rubber the more effort you have to put in your strokes. This is highly inefficient at some point. But no the difference is not high whatsoever. It will just get harder to get a good and consistent ball. If your goal is to better your technique you should definitly...

STN has to be out of the question actually. In terms of control and spin it might be okay. But the incredible low arc is smth you really have to get used to. I played it for several months and had serious issues going back to hurricane. I needes several training sessions to get the ball back on...

Ok a review wont be possible for quite some time because of Covid 19 regulations in germany -.- But a first look/hands on: Actually im pretty disappointed so far from DHS. The blade finish is utterly bad. I mean i already had to sand that blade quite hard. The sides of the handle had carbon...

Asked about that blade a while ago too. No replys and i couldnt find anything review-like on google so i bought it 2 days ago. I will probably write smth about my experience with it after i can play with it again... As for the infos about that: you can find some input on AliExpress. The stores...

I tried the DHS options. Beside a really well boosted and softer Hurricane 3 neo, nothing comes even close to a Tenergy. Maybe the Goldarc Series has some similarities. But that is it. Right now i think the Vega Pro is one of the best alternatives (though i havnt tested the Andro Rasanter...

There are already several posts here about this topic. Neo Version is more receiptive to booster and is overall the better rubber (faster, more spin...) @ArturS if you google for interview with dhs you gonna find the answer on several websites. In short the neo version is slightly factory tuned

He does that for quite some time now. I wouldnt guess he works "against" the tackiness with it but against any form of humidity on the rubber which comes from his breath or his sweat. Either way, the tackiness helps usually to be able to perform their short game. And i highly doubt that Ma Long...

I changed mine now for the fourth time and had several splinters on the sponge. Without sealant it happened with the first change already. Not deep, so i could still use it but visible.

I guess you can go for the Yinhe. Otherwise there are several componies who went the path of the structure of a viscaria/tb or w/e alc. Just browse for it and you can find anything for any budget like 729 blue, dhs tg 506x... For now im sticking with yinhe but i dont really like how the...

Well i guess you cant go much lower with your budget as smth like you already use. Maybe with xiom on your backhand instead of andro. Xiom Vega Pro was my choice for example. And as long as you dont play the national Version on your fh you should be fine here too. Maybe you could go with smth...

I guess Stiga Mantra, Tibhar MX-P, Andro Rasanter R 47 and there might be a decent alternative from Xiom... This board does have Xiom expert. Lets just wait until he arrives, he will know better than in do in at least this case^^

I guess it depends more on how often you gonna reglue or maybe even boost your rubbers if any sealent is needed (besided of the kind of blade you are using - some you really have to seal it). In my experience with several blade - if you glue often and boost, you have to seal that blade...

Just to make it clear before anyone misunderstands this. "Blue is for smash" - These rubbers are damn tacky, and therefore not recommended for smashing at all. If you want to hit with this rubber loop or perform a topsping. Never smash. If you want to smash a really high ball, go and "twiddle"...

They are nearly the same rubber. At least in terms of what you arw asking. The blue one though is way more unforgiving. Hard to predict for the opponent, which is good. But if you play without a developed close to perfect fh technique, the rubber alone will show you that. I wouldnt recommend...

That is pretty much the full magic here you are describing. In comparison to China, Germany for example does nearly nothing for this sport. We have cities who deny the usage of our sport halls in the vacation. On top of that, the amount of money to maintain them is disgustingly low. Scouting...

Big thanks for that insight. There was a lot of interesting information.

I like to disagree here quite hard actually. Nearly every player who plays against FZD frequently is avoiding his fh. If you watch the first games he played in the last 2 tournaments at least, you can see why. They all try to play fh ralleys against him. His backhand though is quite deadly but...

It depends... First of all there is noch good receipt to boost out there, which involves complete undoming. So every boosted rubber has to be domed by the time the tutorial tells you to glue the boosted rubber. Normally you wait for around 1-2 days after your last layer of booster before you...

Has anyone played with the new DHS TG-506X? And could give a quick review/compare it with other blades? https://a.aliexpress.com/_B0djGB https://www.prott.vip/Product-Details.aspx?productcode=TG506X Thank you!

Falco TLB Seamoon doesnt last that long. But everything depends in that department. How often did you already boost that rubber, how often did you play with it, how many layers did you put on. How did you boost the rubber... What im trying to say is that you shouldnt consider what others are...