You can't, it's the Butterfly's deliberate planned obsolescence, every other brand make non damaging glues, go figure... Just DON'T BUY that f******g sh*t glue, plain simple.
There are several ways.
Yes, don't buy Butterfly, Donic, Andro, Tibhar etc glues, they have the same style of bottle and the glue is the same shit in all of them.
You should buy Revolution No3 or DHS No15. If you stack 3-4 layers you can remove them in one go without damaging the sponge. This is also true for cake sponge like Tenergy.
Since now you are in a pickle what you can do is get a solvent and first spread it on the glue and let it get a bit dissolved. After that probably you can remove the glue without much damage to the sponge.
A great solvent would be a booster. Possibly other solvents could be used too like baby oil or something with VOC, but not sure what that will do to your rubbers.
Try to remove the Free Chack sh*t from a D09C and come back later... every other glue does not damage the BTY rubbers, some Stiga sponges like the DNA series are very porous too, the Free Chack kill them too, but it's fine with DHS N°15 or Nittaku FineZip.
A Japan/ESN sponge with that tensor/catapult effect has to be porous, so you'll get the same problem with Rasanters, Tibhar MX or FX series and so on.
The problem is that glue, they know it, but they won't change anything. It's deliberate then.
That's interesting. I actually haven't tried the Free Chack since I heard bad things about this issue and I didn't want to damage my Tenergies. I'm using mainly Tear Mender these days and they come off of D05 and D09C pretty easily. The same couldn't be said about Tear Mender and the Tenergies. I thought I tried DHS #15 with Tenergies a long time ago, but I'll give it another try to see if it's more acceptable now.
NOT GOOD ADVISE to use something with VOC.
Because I could so easily "wash " the glue off my blade using Mineral turpentine , I once used it on the sponge as well.
Have you ever seen a 3mm thick sponge ? 😁
Well, I have to eat some humble pie now.
I went out in my shed and found some epoxy thinners and tried it on a corner cut off from one of my rxton5 rubbers.
Result is that indeed the thinners evaporates quickly and after half a minute the 2 layers of revo3 were soften up to the extend
that i could simply rub it off with my thumb and very little pressure,
Make that 1 : : 0 to Zwilly-boy. 😁
Would I like to try this on a Tenergy ???????????????? Not likely. The Rxton5 sponge is even tenser than an H3 sponge , like cardboard really.
What the same procedure would do on the tensor sponge which has more holes than a swiss cheese, who knows.
If you send me a Tenergy rubber I will gladly try it out, I would have no other use for it anyway 😁
You're living up to your name😂