Just a little sanding. When a blade is sealed too much (which often happens) it is too even and gentle touches can peel the rubber off. A little sanding increases the surface and makes it rougher, holding the rubber better

Top ply sealed? -> sand it a little Rubbers cut with scissors? -> learn to do it properly or use a cutting knife You should not play with it that way and take it off and reglue it as soon as possible. Staying with it will negatively affect playing and will increase the non sticky part quickly

Throw angle and spin will be no problem. Catapult is the biggest concern. EL-S is a quite catapulty and soft (~45 degree) rubber. The best thing about hybrids is, that they are LESS CATAPULTY than previous rubbers. It’s therefore easier to play in short game and more demanding but better quality...

Im not sure whether i understood your description properly. Anyway, for me it really depends on the purpose of the topspin and the amount of time you have for it. In a „rallye“ or training situation like in your video, it’s about consistency and not about winning the point. In a situation...

original True Carbon + bluestar a1 + xxx Dignics 05 is the hardest to exchange. Bluestar a2 in terms of hardness, but it’s a hybrid. Bluestorm pro, bluefire Blabla do not come close

Anyone who played this in the meanwhile and can compare it to hl5 or w968?

Faster and flatter trajectory than Ovtcharov alc from my point of view

Much lower arc than if zlc, much stiffer and quicker for me. Base speed little slower than Viscaria, but much more kick

What a pity Timo didn’t win…

Kanak Jha, who is by faaaaaar the best player in the US, is very average Bundesliga player. No other us-American would be able to play Bundesliga. So, if you consider yourself to be able to become (by far) the best player in the US, you can play Bundesliga. As you’re already 15 years old -...

Those who make it to the Bundesliga usually already play in 2nd or at least 3rd Bundesliga with age of 15. don’t take it too personally, but you won’t make it 😅

Viscaria is outer carbon, wusc is inner carbon Viscaria has hard top ply (koto), wusc has soft top ply (Limba) Viscaria is quite fast, wusc is quite slow „Control“ is very subjective, but from an objective point of view, wusc is much easier to control than Viscaria. If you anyway like to go...

Just once again… he is injured and g1 and r50 are to hard to play for him… The answer for this request can not be a dignics with 50+ hardness guys. It will not be easier for him but at least same hard or even harder. I do not say dignics is a bad rubber, I play it on my own! But it is very...

D05 is probably one of the worst advices ever. It is neither bouncy nor easy to play and takes a lot of effort. If g1 is not easy enough for you, rakza7, c1, r48/r45 might do the trick. They are more bouncy, softer and therefore easier to access

- Donic original True Carbon is a little faster - Xiom alx 36.5 is a little slower - andro syntelliac vco is a little faster - Joola Vyzaryz freeze hrd is a lot faster - Stiga inspira plus is a little faster - DHS is poor quality ( even if a lot of people would disagree, because all the Chinese...

Perhaps because it is not an „inner carbon“ as required

Obviously all table tennis companies do not share your, but my definition. Otherwise they wouldn’t call these rubbers hybrids. It’s about how it plays, not how the rubber behaves when not playing

Because? What does it change, if you have 2 rubbers play exactly the same, one is little tacky, one isn’t. It’s about the properties, not about if you can lift a ball with rubber while not being in a rally. I am 100% sure you would be able to distinguish between c48 with slightly more tackiness...

Repetition number 3627495050: „Hybrid“ does not necessarily mean „sticky topsheet“ and „catapult sponge“. It means, that the playing properties of Chinese and European / Japanese rubbers are combined. Chinese playing properties are: - linear - very slow on low impact (like receive) - very...

Andro rasanter c45, c48, donic bluestar a3,…