like both rubbers are already on but the overhand is kidna crazy but not hanging off enough to use scissors. i also dont have any scissors that are able to cut rubber easily. i have like a box cutter but its not sharp enough nor do i have new blades. i might ask my coach or club to see if they...

sounds like something dhs would do 😂

it was flat until i picked it up. like after the booster dissapeared it was still flat until i picked it up, then it domed. i liked wiped the brush on the lid area where it screws on for about 1 minute and then appliedd. waited till theres was very little left onthe brush

two layers of haifu seamoon. 2nd layer took around the same time. 30 min. but maybe slightly longer for abbout 15 minutes. both of the rubbers were already glued on prior to boosting. i tested them for about a week before deciding to boost. will the splitners cause much damage or change in the...

Hi I just recently boosted my hurricane 3 national at 39˚ hardness (not neo) and a hurricane 3 soft 37˚ (neo) and although people say wait 12-24 hours, somehow the booster dissapeared after 30 min? is that normal? Also, how long will the booster effect last for? Ivermectin reglued my rubbers...

Ah ok thanks. becuase ive reglued my rubbers twice already and there are already splinters on my blade. and i dont have sealant... so im just hoping there will b esome permanent effect so i dont have to reglue often. maybe next time ill get glayzer 09c instead of hurricane. maybe dignics idk.

nah i boosted without the protective sheet on it. will the elasticity or like the speed remain indefinitely or will i eventually have to reboost? like will the effect go away completely or it will retain some extra rebound and elasticity? edit: also do you know why all the booster disspeared...

but for some reason the booster dried after 30-1hr fully?

So i just boosted both of them after trying unboosted for a week and after boosting i did a few bounce test, i did 2 thin layers both sides and waited till there was no more booster left on the surface. then i glued it on and bounce test, it for sure is faster but i didnt know what to expect...

hmm really? doesnt seem to be a problem for me enev though i dont use rozena. perhaps those apsorptive films like the one from butterfly? i think yasaka has one too becuase ive seen ym friend have one but i couldnt find them online.

but non adhesive sheets also stick well and for a long time too and are better than having no protective sheets. they're relatively cheap too. you dont need any brand for non adhesives. just find some off ebay or aliexpress and theyll work.

Yeah you can consider i think butterfly's protetive film i think it was IV adhesive or something along the liens of that. you can also try other brands.

Not from personal experience but i believe freitas is slightly thicker + limba outer ply which should theoretically give it more dwell. viscaria has a koto outer ply which makes it harder and generally faster.

I once again could be wrong but it could be due to tinyt differences in weight or like qc (although butterfly's qc is quite good) or maybe micro differences as there are going to be differences in two blades that are exactly the same e.g. tb alc comapred to another tb alc wont feel the same

I believe it is koto but i could be wrong. you might have to contact butterfly directly to find out.

Perhaps instead of water, you could consider getting a dedicated racket cleaner. and yes you should consider also getting a protector for your backhand. non-adhesive sheets also stick to non-tacky (grippy) rubbers. you could also consider an adhesive sheet but maybe not for tacky rubbers.

I just want t omake it right so i dont ruin 2 rubbers =) but also if i decide to reglue it do i have to remove the glue layer on the blade as well and redo that one?

Haifu Seamoon booster i believe. is two thin layers on fh and 1 thin layer backhand wkth 2 layers of glue both rubbers ok? also do i keep the plastic topsheet protector on? i believe people already answered this but there were a lot of mixed opinions.

BNut after applying the two glue layers do i need to like apply glue again after applying booster? how many layesr of booster do you rec0mmend for 39˚ and 37˚ then? is my initla 2 layers thinly on fh and 1 thin layer bh application to this case?

wait also one more thing, after all iv e heard, should i still do 2 thin layers on forehand and 1 thin layer on backhand or should i do a bit thicker? If i want a setup thats just as fast maybe as dignics 09c but doesnt make it uncontrollable? also when cutting the rubber do i use a knife or...