#579 - Koto / S-AxC / Ayous / Kiri core #580 - Vis structure

#577 - Framiré / Ayous / IC / Ayous core #578 - Black Limba / White Fir / Ayous core

Back to posting custom orders! #568_569 Maze and Vis style compositions. #575_576 A couple of combi cyberthingy oversized blades. Pine / Basalt / Balsa / Cork / Balsa / Cork / Kiri

#1207 - 5 ply - ALL+/OFF- Inspired by a blade I made for a customer, which in turn was inspired by the old Butterfly Powerdrive. However, that one uses an Ayous core, and yes, it's a relatively fast blade, but also quite heavy/head heavy. So, this is a more tamed version with Kiri core, slower...

Oak is quite heavy, so it's not easy to use, even more nowadays when the demand is for lighter and lighter blades, due to heavier rubbers. The grain structure is similar to Koto, but it's heavier and harder. For example, in this blade the outer plies weigh more than the core and composite...

#1174 - 3+2 - OFF+ Thick Oak outer layer for this one, which I never had used. Stiff, crisp and fast with a compact feeling. Available FS. - Oak / TC 200 / Kiri core - 85.4g - 6.1mm - 156x149mm - ST (100x23.5x28.7mm) - Balance: 2.9cm (Low/Med)

#1159 - Outer VC - ALL+/OFF- This blade is a perfect example, just because two blades have a similar structure, doesn't mean they will feel and perform the same, the building process is much more important! In this case, I wanted to make a soft Vis, but frankly I might have overdone it 😅. I...

#1192 - Inner VC - OFF-/OFF Typical inner composition, but using a new fabric: all black Vectran-Carbon. This VC fabric is very close to the blue/black stuff, just slightly stiffer because the weave pattern isn't exactly the same, so this blade plays like your usual inner force ALC. Available...

#1177 - Outer Aramid - OFF-/OFF Based on a Hugo Hal, I'm not sure what density they are using for their composite on the original, but on this one I used a light Aramid fabric, so the blade retains a very woody feeling. Avalable FS. - Koto / Aramid / Limba / Kiri core - 90.0g - 5.9mm -...

#1176 - Outer SALC - OFF/OFF+ Nothing very unusual about this one, just an outer SALC blade with Limba top ply. Available FS. - Limba / SALC / Ayous / Kiri core - 86.3g - 5.9mm - 157x150mm - ST (100x28.5x23.7mm) - Balance: 3.0cm (Med)

#1175 - 3+2 - ALL+ This is a blade that was meant for a customer, but believe or not, it turned out too heavy and too high balanced 😅. It's a stiff blade, especially considering the speed range, but it has a soft feel. Contrary to the blade I posted last, this one should pair well with softer...

#1171 - Inner S-AC - OFF Not very far from the usual inner fiber structure, but here I replaced the core for Kiri, mostly for weight savings. Kiri is less dense than Ayous, so it does not give as much kick on harder shots, for that reason inner fiber blades with Kiri core are not that common...

Because the medial layers are still quite dense on this one, and that also contributes to some extent as they are thicker on this composition. However, you are just looking at the weight, and not the balance. With a lighter handle, about the same weight as DHS uses for example, this blade would...

Padauk! And it will only look better with use 🙂 Yes, it's gone...

#1170 - Outer ALC - OFF This is an attempt at a "Golden Vis". Not claiming it plays like one, but it's my interpretation of the blade, based on what I know from it. Unfortunately I haven't used one yet, so all I know about the blade is from user feedback, which can even be contradictory at...

OK, then that's a different story. I will get back to you over pm.

That's why I always say that I don't make clones. I've had customers send me their blades, but I think it was always to clone the shape or handle, not exactly the composition. In order to perfectly clone a composition, I would have to know exactly everything that's going on at the factory, and...

I will answer to your pm here because I think everyone can benefit from the information. Cloning a specific blade model is one thing, it is certainly possible but there's no guarantee it will be just like your specific specimen. These models have a big variation even within themselves, that may...

I believe so, but I'm not sure 😅. They use a 100g/m2 TC if I'm not mistaken, I had one for repair here but it was a long time ago, so I'm not sure. No. Even if thin, 200g/m2 is already a high density for a carbon layer so you will have some of that frying pan feel.