I did more than a month of using constantly MK on a backhand - 20 hours per week and it’s perform like new almost. So I ordered a few more since it has much of respectable durability. And also I find blue one is slightly harder and faster than red. Black I never tried 🙂

It’s just had glue on it and some kind of more lively sponge now. But I don’t think that newer batches is factory boosted like they stated. Rubber need to be boosted anyway

Thanks! I’m gonna ask today but from what I remember it’s one layer on both D09c/05. And the blade is ZJK SZLC

I like to trying out new stuff - that’s the part of tt that I enjoyed too, my coach is pretty conservative in this - all of the guys our team are using Dignics/Tenergy ( one guy that had highest national rank that is about 35 points in Ukraine system that is about about 2200 in usatt - is using...

I’m not disagreeing guys, I’m telling that for now I need some time to adjust. And the only thing that was unusual is this exercise in comparison with D09c. I can hit really hard so the problem was not the sponge engaging rather I need to find out and working on proper for h3 stroke brushing...

I can loop with anything really. If it better for pros it’s not meaning that is better for everyone else automatically. Same goes with the blades - if Ma Long used w968 then it’s automatically the best blade for everyone? No it’s not of course. I think it’s not the case - it’s matter of...

Yes, when we performed this kind of exercise today - looping to looping far from the table with coach - I performed significantly worse than usual. My first thoughts were maybe this is the day when I’m not feeling the ball. But then I picked my other racket with new D09c and it goes other way...

So guys, I did a three hours of training. Half of them exercises - another one training matches. Few observations about H3 - I’m glad I boost it, it less sticky than my D09c for some reason. It is more safer rubber if I can say so. There is some angles when you loop with D09c sometimes it is...

It should be my rest day (it means only gym and serve practice) but I can’t stand to go and try out H3. So i did gym session and on my way to the tennis club 🫡

It’s just bad durability that’s all. Yesterday I have shown my k3 rubber to a club mate and asking him - how much do you think it is in use? He told - about six months? And it’s 10 days actually. And I don’t mind if it shows signs of wearing but performs good - like D09c for example. The...

I have MK hybrid on three different blades and I wouldn’t say it have pure durability. K3 is other way - very poor durability. But I guess something similar to MK hybrid is Victas v20

You mean some weight?

Hehe, not really, I’m sorry. And we’re so far from each other that there is no point to even buy something like that - easier to buy a new one🤓. But one of my teammates owned that blade because he started to develop a penhold grip - he adapted pretty quickly from his previous shakehand and...

I got all of those besides Lebrun 🙃

I was not applying first layer properly. Only after it got dry I saw that places where I was not so precise with amount of Sea Moon looked differently. Second layer was much cleaner but first one ruined it a bit already and nothing I could do. But it would be my lesson 😁

It is a good blade. I did topspin’s/blocking - nice crisp feeling and control is very high. I don’t now why they called it “the fastest Nittaku blade” - it is far from the speed of Viscaria SALC for example. Very comfortable handle - not too big not too small and nicely fit in the hand.

High level beginner - not bad 😎 I saw a 9 year old boy today that is no1 under 11 years and he had about 2300 rating already - that is high level beginner I suppose 🤣

Thank you for your response and advices. Ovtcharov alc is really not like regular inner force it’s closer to the outer in terms of feeling and speed. I have played with different outer composition for the last year or more. I mostly used Viscaria SALC/FZD ALC/LGY ALC/Ovtcharov ALC all of them...

I have glued the rubber - it was not so easy considering me doing it for the first time - so it’s looked not so fancy as it can be probably. I did serving a bit - it was very easy to serve short. Will trying it out fully tomorrow in the training hall 🫡 The rubber looks like

I will not be waiting until it uncurl. Just will wait about 12-20 hours after adding a second layer as @Master Capybara suggest me