Oh, ok, read it wrong, I'm sorry. It doesn't need to be outside, I shipped a blade to Singapore and it gained 4g just due to different conditions. It was made in the summer during hot and dry weather, and Singapore is very humid. But that one had a Padauk handle, it soaks water like a sponge...

"In my experience wood dries with time unless exposed to humidity." This is a very vague observation, it will depend on the original moisture content and environmental humidity. It doesn't have to be a sauna, any environmental change will cause wood to gain/loose moisture. That's why wood is...

I didn't measure the balance before but on of the reasons I made the weight relief was to compensate for the loss of mass in the head and keep the original balance. The balance after the fix is 3.2cm which is common for commercial blades. Sent from my MAR-LX1A using Tapatalk

Firstly I just wanna say sorry for the watermark, it seems that there are some people who like to steal my repair pics and claim them as their own. A friend of mine asked me to fix his old Primorac Carbon that was in storage for some time. The blade was in pretty bad shape with some severe...

Lately I've been getting a few requests to make something similar to Butterfy's Liu Shiwen blade which is discontinued. Well, unfortunately I don't work with plain zylon, but this has been my suggestion. An over-sized, relatively fast and high throw blade that retains a nice woody feeling. It's...

Definitely not beautiful, also very moody and with a big personality, but we still love her (the cat not the blade :))

This one is available, the blade not the cat :D The blade is based on an Acoustic, built with hide glue but I used two thinner Limba medial plies instead of a thicker one, so this is technically a 7 ply. Composition: Limba / Limba / Limba / Kiri / Limba / Limba / Limba Weight: 91.8g Thickness...

One of my personal favorites, too bad I didn't get to keep it! I must say I don't get any credit for designing this handle, it all came from the owner's mind, I just executed his idea. Composition: Framiré / Ayous / I-C / Ayous / I-C / Ayous / Framiré Weight: 84.6g Thickness: 5.7mm Freq...

I don't think he scammed anybody, or at least that it was his intention. And of course it was only my opinion, based on facts, but still just my opinion. Manufacturers use the term ALC loosely, and I don't mean just blade builders, there are also some brands using Diolen-Carbon in their blades...

Thank you!

Diolen is softer so it does everything a little less. Less speed, smaller sweetspot, but it can give more control depending on the perspective. It also feels a little different, not so dynamic and crisp, more numb perhaps?

I'm guilty of using this in the beginning without knowing what it really was. After I found out I stopped calling it ALC and just use the real name. I still use it from time to time. The darker blue is a give away, it can also be Dyed in several different colors, but the way the fibers fray on...

Medial ply is most definitely Limba, but the Viscaria doesn't have a Limba medial and that's not ALC. That's "chinese ALC" aka Diolen-Carbon, many manufactures use and knowingly or unknowingly call it ALC. Nothing wrong with Diolen if you disclose what it is, but it's not the same as ALC.

I used to work with guitars but I never worked with violins before, let alone three! A commissioned blade with a Violin composition and a cool custom Cobra Kai logo, as well as some simple repairs on a couple of damaged Violins. Composition: Ash / Ash / Kiri / Ash / Ash Weight: 85.3g Thickness...

There aren't many inner fiber blades with Kiri core out in the market and I really don't know why... They can be very good blades! Composition: Hinoki / Ayous / Super A-C / Kiri / Super A-C / Ayous / Hinoki Weight: 82g Thickness: 5.95mmFreq.: 1485 Hz Balance: 1.8cm (very low)

Speed is greatly influenced by stiffness, and the stiffness acts as an whole, so in most blades it will be the same for both sides no matter what the composition is. However, you can still change the hardness and other variables a bit, and that is where the speed difference lies. There was a...

Thanks Basmundo. Well, the player uses inverted on the Fh and long pips on the Bh and has been playing with a Stiga Allround Evolution. He plays a pushblocking game but likes to attack with the Fh and he was looking for something as slow, or even slower than his AE on the Bh, but faster on the...

Thank you for the compliment and encouraging words! Sure, I would love to hear it, I always welcome new challenges.

Thanks :)

This blade is definitively in the top 5 of the most complex requests I have gotten so far. Combi blades are hard, that's a given, but this time the owner presented a full professional project for the blade and handle design! I had to scratch my head a few times to make this one happen, but in...