Not necessarily. The higher the rating the higher the possible spin is. If it is difficult to set spin but You can get a lot, the rubber is NOT spin sensitive. If it is easy to set spin on it regardless of the top capability the rubber is spin sensitive. Some rubbers have a really high maximum...

Hard rubbers are less reactive in the slow game... Cheers L-zr

Keep in mind that T05 FX makes life extremely difficult when it comes to the short and slow game due to its catapult. This goes to a certain extent to normal T05 as well. I would choose a different rubber than butterfly, but if You must, choose Rozena. For now stay away from Tenergy 05 in any...

I think tackiness is a property of the top sheet and the sponge doesn't matter... Cheers L-zr

That's sad, You do have a trainer in the club? Ask the trainer to pair You during training. Then after some time You will get to know the people and then everything will be much better. I know myself that I don't particularly want to train with a beginner, but luckily we don't have many of...

No, they stay, If it was glued by Dandoy I would definitely return it. Cheers L-zr

This happened when You glued it, some speck on the surface is enough. You have to be clean when gluing. Probably used an old (and dirty) sponge to spread the glue. Cheers L-zr

"should I try innerforce ALC-s" I think it would be much too slow and mushy for You. Cheers L-zr

And it was actually an underspin... Gozo, your hitting the ball too late, try to hit it earlier... Cheers L-zr

I really like G09C as well and normal glazer too. Cheers L-zr

I must say that switch was one of best things I ever did. I have much much more control over my FH now with Hurricane 3. The only thing is that it’s a challenge from position 3, but from that position I lost most balls anyway an d I try to stay in position 1 and 2 (closer to the table). I must...

More than you think. A thin crisp blade will vibrate more than a soft one. A softer one will have one huge one like a trampoline. Also the rubber will have a dampening effect. But you are right it’s not a big deal. What you feel is the blade taking up energy from the hit. A stiff hard blade...

But the Hammond has a really soft feel to it. Feels like 45 shore O. Hybrid MK definitely feels harder… Cheers L-zr

My suggestion would be Tibhar hybrid MK. Cheers L-zr

It’s in your head, there is not much difference between those 3 blades. As far as vibration goes, I want a little, but not as much as the Donic Appelgren all play. My Stiga Allround evolution is slower than my Yasaka Sweden but none of them vibrates too much. For a standard Ayous Limba limba...

It’s not that expensive comparing the never ones. But if you find a Chinese rubber with similar characteristics let me know. The closest I get is lightly boosted H3. provincial OS, but that not much cheaper unless You get it on special… Cheers L-zr

1. Most ESN rubbers are NOT “factory boosted” 2. If you can’t handle the harness there is always a softer one. 3. The boosting does NOT evaporate. It is oil and dies not evaporate quickly. Take some of it and put in a bowl and you will see for yourself. What booster does is that it basically...

It could be a speck of something that was present at the time of gluing. It is definitely NOT between sponge and rubber. This happens to me when I don't spread the rubber evenly or even if the layer is too thick. Cheers L-zr

Control is relative to how good You are. You will get more control with a slow rubber. Most Chinese rubbers are slower than most ESN rubbers, so yes You can say that You will get more control with a Chinese rubber. Of course You also have to take into consideration how spin sensitive they are...

Naaa, not G09C on BH, way too hard and slow for this, but perfect on FH… Cheers L-.zr