Thanks, If I saw your post earlier I would order glazyer or dignic 05/80 but I didn’t want to trigger thread twice, waited until trying 09c at first. First, I’ve played dignics 09c on my backhand at a match night (without training session) adaptation was not hard. Tldr: it is much faster...

It do not recommend this setup for backhand, rakza z + 5ply soft wood will make easier to play on short game, but it will require a quite much effort to make decent shot away from table.

After using around 4-5 months, it has shrink a bit, and was not flat (like uncurled), probably small factory boosting effect vanished. Sponge is not very durable like hurricanes or donic c2 for glue removal to re-glue

sometimes I do too, especially in matches, and I want to wrap some band around my self like photo below :D

For that reason, I thought at first Tenergy 19 which seems bit less bouncy then 05's (I've tried t05 and fx 10 some years ago) I'm not sure about my self to control dignics 05 or Dignics 80 over table. All in all, it comes back to skill and training issue but Hybrid rubbers gives more tolerance...

I hope so, I'm familiar with active blocking from rakza z and h3 on FH, I'm glad with my blocks. But it's hard to give speed on dead balls with blocked wrist for me, especially in the match If I'm out of position or miss the timing. I will keep in mind!

Thanks for all suggestions. I've purchased D09C 2.1, I hope it will work on my backhand after Rakza Z 2.0 I know my backhand is not good, trying to get training. Even my technique is not so bad, my consistency is lower and in match conditions my wrist get stressed, not relaxed. So getting...

2. Cuz I like inner carbon even viscaria is tempting for crispness, and primorac’s control paradise where I dream to land every shot with it. All these rubbers are similar for me, eventually they will be replaced with h3 or hybrid rubbers so, primorac would be too slow, viscaria will be too...

I also agree on that, I have some decent backhand, but not that good of course. Although I work on it with trainings, I think I can’t ever reach that level. Sorry for misunderstanding, I’ve used t05 on TB alc. other rubbers have been tried on long 5. As d09c is faster than rakza z, it could...

I don’t think so, If you don’t want to really slow down. My long 5 89-90gr, acoustic 88-89gr. Although acoustic headsize is 2mm is shorter which makes difference but I think thinner or lighter rubbers makes more difference. G1 is heavy rubber. For counterspin, hybrid or chinese rubbers makes it...

I have both long 5 and Nittaku acoustic, If you want to increase consistency, it may help. But I don’t think your fh topspins with acoustic won’t be much stronger than long5.

Thanks, I've checked, I couldn’t found Yinhe in european retailers. Right, tenergy 19 would not be so different than 05 (although I played 10 years ago with celluloid 40 ball) probably I will stick with rakza z bit longer when considering tenergy like rubber’s bounciness.

Hello, I’ve been using rakza z on BH for a while, I’m happy especially receive and block, not much complaint except speed. But it feels too slow, even 1 meter away table, I’m making much effort for a decent shot, even I don’t mention openin against backspin. I’m thinking to switch to a bit...

Acoustic SG 24.5 x 33.5 Long 5 26 x 33 Bo Carbon 24 x 34.5 At first I've thought it maybe similar to long5 or w968 but Acoustic G-revision says 24.5 and photo seems its wider than regular Acoustic. And there are no SG handle in their product list, so as I understand they...

Maybe Yasaka rakza Z Although I don’t recommend for backhand away from table.

I am not sure for the rest but 0 force should equal to 0 speed for any type of rubber, unless you have jedi powers.

Dima 11-5 Dan

@Wrighty67 Thank you. I don't have a caliper but from my rough measurements. Fang Bo Carbon ~24 mm HL 3 ~27mm I've ordered HL 5 recently, from the pictures above It looks like very similar to Fang Bo Carbon. I will update here when I get the blade for future reference. As I understand W968...

Wrighty67 Could you also add dimensions for thickness? I would like to compare with HL3 and FB carbon.

They just break in couple session, then they start playing normally. Some rubbers takes more time. I guess pro’s have some ways to make ready faster like swipe until less tacky etc.